SG2 PM Stainless Steel – Solid (.14″ X 19-3/4″ X 1-1/2″)

Product for SG2 PM Stainless Steel – Solid (.14″ x 19-3/4″ x 1-1/2″)

Maker: Takefu Special Steel (click to see more by this maker)

Price: $399.72

Item num: 100977

Total length: 19.75 in.
Item weight: 22.80 oz.
Size: 3.6mm x 19-3/4″ x 1-1/2″
Style: Stainless steel bar

: This 3.6mm thick bar of Solid SG2 PM stainless steel is cut to 19-3/4 inches long and is 1-1/2 inches wide.
SG2 (Super Gold 2) is powdered metallurgical steel with a fine grain structure. SG2 is free from impure substances and achieves good abrasion resistance. The addition of 15% Cr (chromium) provides good corrosion resistance while 2.8% Mo (molybdenum) makes a stronger substrate (matrix) and helps prevent carbides from dropping out of solution during heat treatment. The addition of V (vanadium) creates finer grain. The added Cr, Mo, and V form many hard carbides, so abrasion resistance improves. Fine grain and abrasion resistance gives knives long-term edge holding ability with a very keen, clean, cutting edge. SG2 is easily machinable, it is forgeable, and is also easy to grind and finish. SG2 is one of the highest performing stainless steels on the market today.

SG2 Specs
C	CR	Mo	V
1.4%	15.0%	2.0%	2.8%

Heat Treatment
Forging: Forge at 1100°C/2012°F. Do not forge below 1000°C/1832°F. You should anneal after forging. SG2 can be forged using good forging practice.
Annealing: Anneal at 880°C/1616°F. Cooling speed should not exceed 25°C/hr – 77°F/hr
Quenching: Quench at 1050-1100°C/1922-2012°F. Quench in oil (50°C/122°F) or air (25°C/77°F)
Tempering: Temper at 150-250°C (302-482°F). If you coat such as TiC, temper at 550°C/1022°F

Hardness
Annealed: Hrc 30
Hardened: Hrc 62
Sub-Zero: Hrc 62.5

Mastersmith Bill Burke’s Heat Treatment Recommendation: After forging/annealing, grind blade to 220 grit (120 grit minimum) finish. Wrap in high temp stainless foil, being sure to seal air tight. Place blade in heat treat oven and ramp oven to 1560 °F and hold 30 minutes. Ramp oven to 2012°F and hold a maximum of 10 minutes. Air, oil or plate quench. Subzero quench at -112°F to -300°F for 60 minutes. Temper two times for two hours each cycle for desired hardness at 300 – 480°F.

Note: results may vary with hardening method and section size. Salt or oil quenching will give maximum results. Vacuum or atmosphere cooling may result in up to 1-2 Hrc lower.